R60802 Alloy vs. ACI-ASTM CA15M Steel

R60802 alloy belongs to the otherwise unclassified metals classification, while ACI-ASTM CA15M steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60802 alloy and the bottom bar is ACI-ASTM CA15M steel.

UNS R60802 Zirconium-Tin Alloy ACI-ASTM CA15M (J91151) Cast Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		98
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		22
Elongation at Break, %		20

Poisson's Ratio		0.34
Poisson's Ratio		0.28

Shear Modulus, GPa		36
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		430
Tensile Strength: Ultimate (UTS), MPa		690

Tensile Strength: Yield (Proof), MPa		270
Tensile Strength: Yield (Proof), MPa		510

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		270

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		480

Thermal Conductivity, W/m-K		22
Thermal Conductivity, W/m-K		27

Thermal Expansion, µm/m-K		6.0
Thermal Expansion, µm/m-K		10

Otherwise Unclassified Properties

Density, g/cm³		6.5
Density, g/cm³		7.8

Embodied Water, L/kg		290
Embodied Water, L/kg		100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		85
Resilience: Ultimate (Unit Rupture Work), MJ/m³		130

Resilience: Unit (Modulus of Resilience), kJ/m³		380
Resilience: Unit (Modulus of Resilience), kJ/m³		670

Stiffness to Weight: Axial, points		8.3
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		25

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		22

Thermal Diffusivity, mm²/s		12
Thermal Diffusivity, mm²/s		7.2

Thermal Shock Resistance, points		53
Thermal Shock Resistance, points		25

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.15

Chromium (Cr), %		0.050 to 0.15
Chromium (Cr), %		11.5 to 14

Iron (Fe), %		0.070 to 0.2
Iron (Fe), %		82.1 to 88.4

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.15 to 1.0

Nickel (Ni), %		0.030 to 0.080
Nickel (Ni), %		0 to 1.0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0
Silicon (Si), %		0 to 0.65

Sulfur (S), %		0
Sulfur (S), %		0 to 0.040

Tin (Sn), %		1.2 to 1.7
Tin (Sn), %		0

Zirconium (Zr), %		97.8 to 98.7
Zirconium (Zr), %		0

Residuals, %		0 to 0.11
Residuals, %		0