R60802 Alloy vs. ACI-ASTM CB6 Steel

R60802 alloy belongs to the otherwise unclassified metals classification, while ACI-ASTM CB6 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60802 alloy and the bottom bar is ACI-ASTM CB6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 22
18
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 36
77
Tensile Strength: Ultimate (UTS), MPa 430
880
Tensile Strength: Yield (Proof), MPa 270
660

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 22
17
Thermal Expansion, µm/m-K 6.0
10

Otherwise Unclassified Properties

Density, g/cm3 6.5
7.8
Embodied Water, L/kg 290
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 85
150
Resilience: Unit (Modulus of Resilience), kJ/m3 380
1110
Stiffness to Weight: Axial, points 8.3
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 18
32
Strength to Weight: Bending, points 19
26
Thermal Diffusivity, mm2/s 12
4.6
Thermal Shock Resistance, points 53
31

Alloy Composition

Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0.050 to 0.15
15.5 to 17.5
Iron (Fe), % 0.070 to 0.2
74.4 to 81
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0.030 to 0.080
3.5 to 5.5
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.2 to 1.7
0
Zirconium (Zr), % 97.8 to 98.7
0
Residuals, % 0 to 0.11
0