R60802 Alloy vs. AISI 205 Stainless Steel

R60802 alloy belongs to the otherwise unclassified metals classification, while AISI 205 stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60802 alloy and the bottom bar is AISI 205 stainless steel.

UNS R60802 Zirconium-Tin Alloy AISI 205 (S20500) Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		98
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		22
Elongation at Break, %		11 to 51

Poisson's Ratio		0.34
Poisson's Ratio		0.28

Shear Modulus, GPa		36
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		430
Tensile Strength: Ultimate (UTS), MPa		800 to 1430

Tensile Strength: Yield (Proof), MPa		270
Tensile Strength: Yield (Proof), MPa		450 to 1100

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		280

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		6.0
Thermal Expansion, µm/m-K		18

Otherwise Unclassified Properties

Density, g/cm³		6.5
Density, g/cm³		7.6

Embodied Water, L/kg		290
Embodied Water, L/kg		150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		85
Resilience: Ultimate (Unit Rupture Work), MJ/m³		150 to 430

Resilience: Unit (Modulus of Resilience), kJ/m³		380
Resilience: Unit (Modulus of Resilience), kJ/m³		510 to 3060

Stiffness to Weight: Axial, points		8.3
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		26

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		29 to 52

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		25 to 37

Thermal Shock Resistance, points		53
Thermal Shock Resistance, points		16 to 29

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0.12 to 0.25

Chromium (Cr), %		0.050 to 0.15
Chromium (Cr), %		16.5 to 18.5

Iron (Fe), %		0.070 to 0.2
Iron (Fe), %		62.6 to 68.1

Manganese (Mn), %		0
Manganese (Mn), %		14 to 15.5

Nickel (Ni), %		0.030 to 0.080
Nickel (Ni), %		1.0 to 1.7

Nitrogen (N), %		0
Nitrogen (N), %		0.32 to 0.4

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.060

Silicon (Si), %		0
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tin (Sn), %		1.2 to 1.7
Tin (Sn), %		0

Zirconium (Zr), %		97.8 to 98.7
Zirconium (Zr), %		0

Residuals, %		0 to 0.11
Residuals, %		0