R60802 Alloy vs. Grade 8 Babbitt Metal
Both R60802 alloy and grade 8 Babbitt Metal are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is R60802 alloy and the bottom bar is grade 8 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 24 |
| Poisson's Ratio | 0.34 | |
| 0.41 |
| Shear Modulus, GPa | 36 | |
| 8.5 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 23 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 46 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 150 |
| Thermal Conductivity, W/m-K | 22 | |
| 24 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 24 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.5 | |
| 10 |
| Embodied Water, L/kg | 290 | |
| 840 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
| 11 |
| Stiffness to Weight: Axial, points | 8.3 | |
| 1.3 |
| Stiffness to Weight: Bending, points | 23 | |
| 9.2 |
| Thermal Diffusivity, mm2/s | 12 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 14 to 16 |
| Arsenic (As), % | 0 | |
| 0.3 to 0.6 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.050 to 0.15 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 0.070 to 0.2 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 77.1 to 81.2 |
| Nickel (Ni), % | 0.030 to 0.080 | |
| 0 |
| Tin (Sn), % | 1.2 to 1.7 | |
| 4.5 to 5.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Zirconium (Zr), % | 97.8 to 98.7 | |
| 0 |
| Residuals, % | 0 to 0.11 | |
| 0 |