R60802 Alloy vs. N06210 Nickel

R60802 alloy belongs to the otherwise unclassified metals classification, while N06210 nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R60802 alloy and the bottom bar is N06210 nickel.

UNS R60802 Zirconium-Tin Alloy UNS N06210 Nickel Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		98
Elastic (Young's, Tensile) Modulus, GPa		220

Elongation at Break, %		22
Elongation at Break, %		51

Poisson's Ratio		0.34
Poisson's Ratio		0.29

Shear Modulus, GPa		36
Shear Modulus, GPa		85

Tensile Strength: Ultimate (UTS), MPa		430
Tensile Strength: Ultimate (UTS), MPa		780

Tensile Strength: Yield (Proof), MPa		270
Tensile Strength: Yield (Proof), MPa		350

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		330

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		420

Thermal Expansion, µm/m-K		6.0
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		6.5
Density, g/cm³		9.0

Embodied Water, L/kg		290
Embodied Water, L/kg		310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		85
Resilience: Ultimate (Unit Rupture Work), MJ/m³		320

Resilience: Unit (Modulus of Resilience), kJ/m³		380
Resilience: Unit (Modulus of Resilience), kJ/m³		280

Stiffness to Weight: Axial, points		8.3
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		24

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		53
Thermal Shock Resistance, points		22

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.015

Chromium (Cr), %		0.050 to 0.15
Chromium (Cr), %		18 to 20

Cobalt (Co), %		0
Cobalt (Co), %		0 to 1.0

Iron (Fe), %		0.070 to 0.2
Iron (Fe), %		0 to 1.0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		18 to 20

Nickel (Ni), %		0.030 to 0.080
Nickel (Ni), %		54.8 to 62.5

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0
Silicon (Si), %		0 to 0.080

Sulfur (S), %		0
Sulfur (S), %		0 to 0.020

Tantalum (Ta), %		0
Tantalum (Ta), %		1.5 to 2.2

Tin (Sn), %		1.2 to 1.7
Tin (Sn), %		0

Vanadium (V), %		0
Vanadium (V), %		0 to 0.35

Zirconium (Zr), %		97.8 to 98.7
Zirconium (Zr), %		0

Residuals, %		0 to 0.11
Residuals, %		0