R60802 Alloy vs. N10665 Nickel

R60802 alloy belongs to the otherwise unclassified metals classification, while N10665 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60802 alloy and the bottom bar is N10665 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
220
Elongation at Break, % 22
45
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 36
84
Tensile Strength: Ultimate (UTS), MPa 430
860
Tensile Strength: Yield (Proof), MPa 270
400

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 22
11
Thermal Expansion, µm/m-K 6.0
10

Otherwise Unclassified Properties

Density, g/cm3 6.5
9.3
Embodied Water, L/kg 290
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 85
320
Resilience: Unit (Modulus of Resilience), kJ/m3 380
360
Stiffness to Weight: Axial, points 8.3
13
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 18
26
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 12
3.1
Thermal Shock Resistance, points 53
27

Alloy Composition

Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0.050 to 0.15
0 to 1.0
Cobalt (Co), % 0
0 to 1.0
Iron (Fe), % 0.070 to 0.2
0 to 2.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0.030 to 0.080
64.8 to 74
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 0.1
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.2 to 1.7
0
Zirconium (Zr), % 97.8 to 98.7
0
Residuals, % 0 to 0.11
0