R60804 Alloy vs. C43500 Brass
R60804 alloy belongs to the otherwise unclassified metals classification, while C43500 brass belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is R60804 alloy and the bottom bar is C43500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 110 |
| Elongation at Break, % | 22 | |
| 8.5 to 46 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 36 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 320 to 530 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 120 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 380 |
| Thermal Conductivity, W/m-K | 22 | |
| 120 |
| Thermal Expansion, µm/m-K | 6.0 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.5 | |
| 8.5 |
| Embodied Water, L/kg | 290 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 85 | |
| 44 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
| 65 to 1040 |
| Stiffness to Weight: Axial, points | 8.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 10 to 17 |
| Strength to Weight: Bending, points | 19 | |
| 12 to 17 |
| Thermal Diffusivity, mm2/s | 12 | |
| 37 |
| Thermal Shock Resistance, points | 53 | |
| 11 to 18 |
Alloy Composition
| Chromium (Cr), % | 0.070 to 0.13 | |
| 0 |
| Copper (Cu), % | 0 | |
| 79 to 83 |
| Iron (Fe), % | 0.18 to 0.24 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.090 |
| Tin (Sn), % | 1.2 to 1.7 | |
| 0.6 to 1.2 |
| Zinc (Zn), % | 0 | |
| 15.4 to 20.4 |
| Zirconium (Zr), % | 97.8 to 98.6 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |