R60901 Alloy vs. 5088 Aluminum

R60901 alloy belongs to the otherwise unclassified metals classification, while 5088 aluminum belongs to the aluminum alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R60901 alloy and the bottom bar is 5088 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
68
Elongation at Break, % 17 to 22
29
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 37
25
Tensile Strength: Ultimate (UTS), MPa 500 to 580
310
Tensile Strength: Yield (Proof), MPa 350 to 390
150

Thermal Properties

Latent Heat of Fusion, J/g 250
390
Specific Heat Capacity, J/kg-K 270
900
Thermal Conductivity, W/m-K 17
120
Thermal Expansion, µm/m-K 6.3
24

Otherwise Unclassified Properties

Density, g/cm3 6.6
2.7
Embodied Water, L/kg 270
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88 to 100
76
Resilience: Unit (Modulus of Resilience), kJ/m3 640 to 760
170
Stiffness to Weight: Axial, points 8.3
14
Stiffness to Weight: Bending, points 23
50
Strength to Weight: Axial, points 21 to 25
32
Strength to Weight: Bending, points 21 to 24
38
Thermal Diffusivity, mm2/s 9.7
51
Thermal Shock Resistance, points 58 to 67
14

Alloy Composition

Aluminum (Al), % 0
92.4 to 94.8
Chromium (Cr), % 0
0 to 0.15
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 0
0.1 to 0.35
Magnesium (Mg), % 0
4.7 to 5.5
Manganese (Mn), % 0
0.2 to 0.5
Niobium (Nb), % 2.4 to 2.8
0
Silicon (Si), % 0
0 to 0.2
Zinc (Zn), % 0
0.2 to 0.4
Zirconium (Zr), % 96.8 to 97.5
0 to 0.15
Residuals, % 0
0 to 0.15