S13800 Stainless Steel vs. ACI-ASTM CK35MN Steel
Both S13800 stainless steel and ACI-ASTM CK35MN steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is ACI-ASTM CK35MN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 290 to 480 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 11 to 18 | |
| 40 |
| Fatigue Strength, MPa | 410 to 870 | |
| 270 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 650 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 440 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 12 |
| Thermal Expansion, µm/m-K | 11 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 31 |
| Density, g/cm3 | 7.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 5.9 |
| Embodied Energy, MJ/kg | 46 | |
| 81 |
| Embodied Water, L/kg | 140 | |
| 210 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 48 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 240 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 22 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 21 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 3.3 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0.9 to 1.4 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.035 |
| Chromium (Cr), % | 12.3 to 13.2 | |
| 22 to 24 |
| Copper (Cu), % | 0 | |
| 0 to 0.4 |
| Iron (Fe), % | 73.6 to 77.3 | |
| 43.4 to 51.8 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 6.0 to 6.8 |
| Nickel (Ni), % | 7.5 to 8.5 | |
| 20 to 22 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0.21 to 0.32 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.0080 | |
| 0 to 0.020 |