S13800 Stainless Steel vs. ASTM A202 Steel
Both S13800 stainless steel and ASTM A202 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is ASTM A202 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 290 to 480 | |
| 180 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 18 | |
| 17 to 18 |
| Fatigue Strength, MPa | 410 to 870 | |
| 240 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 610 to 1030 | |
| 360 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 590 to 670 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 350 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 410 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 52 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 2.1 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 46 | |
| 19 |
| Embodied Water, L/kg | 140 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 93 to 96 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 330 to 350 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 21 to 24 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 14 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 17 to 20 |