S13800 Stainless Steel vs. EN 1.0213 Steel
Both S13800 stainless steel and EN 1.0213 steel are iron alloys. They have 76% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is EN 1.0213 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 290 to 480 | |
| 92 to 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 18 | |
| 12 to 25 |
| Fatigue Strength, MPa | 410 to 870 | |
| 160 to 240 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 39 to 62 | |
| 72 to 80 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 610 to 1030 | |
| 230 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 320 to 430 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 220 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1470 |
| Melting Onset (Solidus), °C | 1410 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 53 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 46 | |
| 18 |
| Embodied Water, L/kg | 140 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 33 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 120 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 13 to 16 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 14 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 10 to 14 |
Alloy Composition
| Aluminum (Al), % | 0.9 to 1.4 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.050 | |
| 0.060 to 0.1 |
| Chromium (Cr), % | 12.3 to 13.2 | |
| 0 |
| Iron (Fe), % | 73.6 to 77.3 | |
| 99.245 to 99.67 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.25 to 0.45 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 7.5 to 8.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.0080 | |
| 0 to 0.025 |