S13800 Stainless Steel vs. EN 1.3963 Alloy
Both S13800 stainless steel and EN 1.3963 alloy are iron alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is EN 1.3963 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 18 | |
| 29 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Shear Strength, MPa | 610 to 1030 | |
| 290 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 440 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1430 |
| Melting Onset (Solidus), °C | 1410 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 11 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 25 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 4.8 |
| Embodied Energy, MJ/kg | 46 | |
| 66 |
| Embodied Water, L/kg | 140 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 260 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 15 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 16 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 110 |
Alloy Composition
| Aluminum (Al), % | 0.9 to 1.4 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.050 |
| Chromium (Cr), % | 12.3 to 13.2 | |
| 0 to 0.25 |
| Iron (Fe), % | 73.6 to 77.3 | |
| 60.5 to 64.9 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 7.5 to 8.5 | |
| 35 to 37 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.0080 | |
| 0.1 to 0.2 |