S13800 Stainless Steel vs. EN 1.7216 Steel
Both S13800 stainless steel and EN 1.7216 steel are iron alloys. They have 77% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is EN 1.7216 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 290 to 480 | |
| 200 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 18 | |
| 12 to 23 |
| Fatigue Strength, MPa | 410 to 870 | |
| 290 to 440 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 610 to 1030 | |
| 410 to 560 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 650 to 930 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 400 to 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 420 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 46 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 2.4 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 46 | |
| 20 |
| Embodied Water, L/kg | 140 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 110 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 430 to 1280 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 23 to 33 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 21 to 27 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 12 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 19 to 27 |
Alloy Composition
| Aluminum (Al), % | 0.9 to 1.4 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0.27 to 0.34 |
| Chromium (Cr), % | 12.3 to 13.2 | |
| 0.8 to 1.2 |
| Iron (Fe), % | 73.6 to 77.3 | |
| 97.2 to 98.4 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.35 to 0.6 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0.15 to 0.3 |
| Nickel (Ni), % | 7.5 to 8.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.0080 | |
| 0 to 0.035 |