S13800 Stainless Steel vs. R05240 Alloy
S13800 stainless steel belongs to the iron alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is R05240 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 150 |
| Elongation at Break, % | 11 to 18 | |
| 25 |
| Poisson's Ratio | 0.28 | |
| 0.36 |
| Shear Modulus, GPa | 77 | |
| 57 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 190 |
| Thermal Expansion, µm/m-K | 11 | |
| 6.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 14 |
| Embodied Water, L/kg | 140 | |
| 460 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 90 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 13 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 5.4 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 6.8 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0.9 to 1.4 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.010 |
| Chromium (Cr), % | 12.3 to 13.2 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 73.6 to 77.3 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 7.5 to 8.5 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 | |
| 35 to 42 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.0080 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 57.9 to 65 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |