S13800 Stainless Steel vs. ZA-12
S13800 stainless steel belongs to the iron alloys classification, while ZA-12 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is S13800 stainless steel and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 290 to 480 | |
| 89 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 83 |
| Elongation at Break, % | 11 to 18 | |
| 1.6 to 5.3 |
| Fatigue Strength, MPa | 410 to 870 | |
| 73 to 120 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Shear Modulus, GPa | 77 | |
| 33 |
| Shear Strength, MPa | 610 to 1030 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1730 | |
| 260 to 400 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1580 | |
| 210 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 100 |
| Melting Completion (Liquidus), °C | 1450 | |
| 430 |
| Melting Onset (Solidus), °C | 1410 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 16 | |
| 120 |
| Thermal Expansion, µm/m-K | 11 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.4 |
| Embodied Energy, MJ/kg | 46 | |
| 64 |
| Embodied Water, L/kg | 140 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 4.0 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1090 to 5490 | |
| 260 to 620 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 35 to 61 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 28 to 41 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 43 |
| Thermal Shock Resistance, points | 33 to 58 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0.9 to 1.4 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 12.3 to 13.2 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 73.6 to 77.3 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 7.5 to 8.5 | |
| 0 to 0.020 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.060 |
| Sulfur (S), % | 0 to 0.0080 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 87.1 to 89 |