S17400 Stainless Steel vs. AWS ERTi-5
S17400 stainless steel belongs to the iron alloys classification, while AWS ERTi-5 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S17400 stainless steel and the bottom bar is AWS ERTi-5.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 11 to 21 | |
| 10 |
| Fatigue Strength, MPa | 380 to 670 | |
| 470 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 75 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1390 | |
| 900 |
| Tensile Strength: Yield (Proof), MPa | 580 to 1250 | |
| 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 850 | |
| 340 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1610 |
| Melting Onset (Solidus), °C | 1400 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 560 |
| Thermal Conductivity, W/m-K | 17 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 36 |
| Density, g/cm3 | 7.8 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 38 |
| Embodied Energy, MJ/kg | 39 | |
| 610 |
| Embodied Water, L/kg | 130 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 87 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 to 4060 | |
| 3250 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 32 to 49 | |
| 56 |
| Strength to Weight: Bending, points | 27 to 35 | |
| 46 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 2.9 |
| Thermal Shock Resistance, points | 30 to 46 | |
| 63 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.050 |
| Chromium (Cr), % | 15 to 17 | |
| 0 |
| Copper (Cu), % | 3.0 to 5.0 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 70.4 to 78.9 | |
| 0 to 0.22 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 3.0 to 5.0 | |
| 0 |
| Niobium (Nb), % | 0.15 to 0.45 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0.12 to 0.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 88.2 to 90.9 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |