S17400 Stainless Steel vs. Commercially Pure Zirconium
S17400 stainless steel belongs to the iron alloys classification, while commercially pure zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is S17400 stainless steel and the bottom bar is commercially pure zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 11 to 21 | |
| 18 |
| Fatigue Strength, MPa | 380 to 670 | |
| 60 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1390 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 580 to 1250 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 270 |
| Thermal Conductivity, W/m-K | 17 | |
| 22 |
| Thermal Expansion, µm/m-K | 11 | |
| 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.7 |
| Embodied Water, L/kg | 130 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 to 4060 | |
| 290 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 32 to 49 | |
| 18 |
| Strength to Weight: Bending, points | 27 to 35 | |
| 19 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 12 |
| Thermal Shock Resistance, points | 30 to 46 | |
| 56 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.050 |
| Chromium (Cr), % | 15 to 17 | |
| 0 to 0.2 |
| Copper (Cu), % | 3.0 to 5.0 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 70.4 to 78.9 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 3.0 to 5.0 | |
| 0 |
| Niobium (Nb), % | 0.15 to 0.45 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 94.7 to 100 |