S17700 Stainless Steel vs. AWS BAg-24

S17700 stainless steel belongs to the iron alloys classification, while AWS BAg-24 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is S17700 stainless steel and the bottom bar is AWS BAg-24.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
33
Tensile Strength: Ultimate (UTS), MPa 1180 to 1650
150

Thermal Properties

Latent Heat of Fusion, J/g 290
130
Melting Completion (Liquidus), °C 1440
730
Melting Onset (Solidus), °C 1400
660
Specific Heat Capacity, J/kg-K 480
310
Thermal Expansion, µm/m-K 11
21

Otherwise Unclassified Properties

Density, g/cm3 7.7
9.0
Embodied Carbon, kg CO2/kg material 2.8
49
Embodied Energy, MJ/kg 40
770

Common Calculations

Stiffness to Weight: Axial, points 14
5.3
Stiffness to Weight: Bending, points 25
16
Strength to Weight: Axial, points 42 to 59
4.6
Strength to Weight: Bending, points 32 to 40
6.9
Thermal Shock Resistance, points 39 to 54
5.9

Alloy Composition

Aluminum (Al), % 0.75 to 1.5
0
Carbon (C), % 0 to 0.090
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
19 to 21
Iron (Fe), % 70.5 to 76.8
0
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 6.5 to 7.8
1.5 to 2.5
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
49 to 51
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
26 to 30
Residuals, % 0
0 to 0.15