S20431 Stainless Steel vs. EN 1.4589 Stainless Steel

Both S20431 stainless steel and EN 1.4589 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 88% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S20431 stainless steel and the bottom bar is EN 1.4589 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
17
Fatigue Strength, MPa 320
260
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 500
400
Tensile Strength: Ultimate (UTS), MPa 710
650
Tensile Strength: Yield (Proof), MPa 350
440

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 410
470
Maximum Temperature: Mechanical, °C 890
810
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.5
2.4
Embodied Energy, MJ/kg 36
34
Embodied Water, L/kg 140
110

Common Calculations

PREN (Pitting Resistance) 20
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
96
Resilience: Unit (Modulus of Resilience), kJ/m3 310
490
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25
23
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 4.0
6.7
Thermal Shock Resistance, points 15
23

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.080
Chromium (Cr), % 17 to 18
13.5 to 15.5
Copper (Cu), % 1.5 to 3.5
0
Iron (Fe), % 66.1 to 74.4
78.2 to 85
Manganese (Mn), % 5.0 to 7.0
0 to 1.0
Molybdenum (Mo), % 0
0.2 to 1.2
Nickel (Ni), % 2.0 to 4.0
1.0 to 2.5
Nitrogen (N), % 0.1 to 0.25
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.3 to 0.5