S20431 Stainless Steel vs. Grade CW6MC Nickel

S20431 stainless steel belongs to the iron alloys classification, while grade CW6MC nickel belongs to the nickel alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S20431 stainless steel and the bottom bar is grade CW6MC nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
28
Fatigue Strength, MPa 320
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 710
540
Tensile Strength: Yield (Proof), MPa 350
310

Thermal Properties

Latent Heat of Fusion, J/g 280
330
Maximum Temperature: Mechanical, °C 890
980
Melting Completion (Liquidus), °C 1400
1480
Melting Onset (Solidus), °C 1360
1430
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
11
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
80
Density, g/cm3 7.7
8.6
Embodied Carbon, kg CO2/kg material 2.5
14
Embodied Energy, MJ/kg 36
200
Embodied Water, L/kg 140
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
130
Resilience: Unit (Modulus of Resilience), kJ/m3 310
240
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 23
17
Thermal Diffusivity, mm2/s 4.0
2.8
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.060
Chromium (Cr), % 17 to 18
20 to 23
Copper (Cu), % 1.5 to 3.5
0
Iron (Fe), % 66.1 to 74.4
0 to 5.0
Manganese (Mn), % 5.0 to 7.0
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 2.0 to 4.0
55.4 to 68.9
Niobium (Nb), % 0
3.2 to 4.5
Nitrogen (N), % 0.1 to 0.25
0
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030