S20432 Stainless Steel vs. 4032 Aluminum

S20432 stainless steel belongs to the iron alloys classification, while 4032 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is 4032 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
120
Elastic (Young's, Tensile) Modulus, GPa 200
73
Elongation at Break, % 45
6.7
Fatigue Strength, MPa 210
110
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
28
Shear Strength, MPa 400
260
Tensile Strength: Ultimate (UTS), MPa 580
390
Tensile Strength: Yield (Proof), MPa 230
320

Thermal Properties

Latent Heat of Fusion, J/g 280
570
Maximum Temperature: Mechanical, °C 900
180
Melting Completion (Liquidus), °C 1410
570
Melting Onset (Solidus), °C 1370
530
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 15
140
Thermal Expansion, µm/m-K 17
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
34
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
120

Otherwise Unclassified Properties

Base Metal Price, % relative 13
10
Density, g/cm3 7.8
2.6
Embodied Carbon, kg CO2/kg material 2.7
7.8
Embodied Energy, MJ/kg 38
140
Embodied Water, L/kg 140
1030

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
25
Resilience: Unit (Modulus of Resilience), kJ/m3 140
700
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
53
Strength to Weight: Axial, points 21
41
Strength to Weight: Bending, points 20
45
Thermal Diffusivity, mm2/s 4.0
59
Thermal Shock Resistance, points 13
20

Alloy Composition

Aluminum (Al), % 0
81.1 to 87.2
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 18
0 to 0.1
Copper (Cu), % 2.0 to 3.0
0.5 to 1.3
Iron (Fe), % 66.7 to 74
0 to 1.0
Magnesium (Mg), % 0
0.8 to 1.3
Manganese (Mn), % 3.0 to 5.0
0
Nickel (Ni), % 4.0 to 6.0
0.5 to 1.3
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
11 to 13.5
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.15