S20433 Stainless Steel vs. CC332G Bronze

S20433 stainless steel belongs to the iron alloys classification, while CC332G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S20433 stainless steel and the bottom bar is CC332G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
130
Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 46
22
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
43
Tensile Strength: Ultimate (UTS), MPa 630
620
Tensile Strength: Yield (Proof), MPa 270
250

Thermal Properties

Latent Heat of Fusion, J/g 280
230
Maximum Temperature: Mechanical, °C 900
220
Melting Completion (Liquidus), °C 1400
1060
Melting Onset (Solidus), °C 1360
1010
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 17
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
12

Otherwise Unclassified Properties

Base Metal Price, % relative 13
29
Density, g/cm3 7.7
8.3
Embodied Carbon, kg CO2/kg material 2.7
3.4
Embodied Energy, MJ/kg 39
55
Embodied Water, L/kg 150
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 180
270
Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 14
21

Alloy Composition

Aluminum (Al), % 0
8.5 to 10.5
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 18
0
Copper (Cu), % 1.5 to 3.5
80 to 86
Iron (Fe), % 64.1 to 72.4
1.0 to 3.0
Lead (Pb), % 0
0 to 0.1
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 5.5 to 7.5
0 to 2.0
Nickel (Ni), % 3.5 to 5.5
1.5 to 4.0
Nitrogen (N), % 0.1 to 0.25
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0 to 0.2
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.5