S20910 Stainless Steel vs. SAE-AISI 1015 Steel
Both S20910 stainless steel and SAE-AISI 1015 steel are iron alloys. They have 58% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S20910 stainless steel and the bottom bar is SAE-AISI 1015 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 to 290 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 14 to 39 | |
| 20 to 32 |
| Fatigue Strength, MPa | 310 to 460 | |
| 170 to 250 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 56 to 62 | |
| 46 to 56 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Shear Strength, MPa | 500 to 570 | |
| 260 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 940 | |
| 390 to 440 |
| Tensile Strength: Yield (Proof), MPa | 430 to 810 | |
| 210 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1080 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1470 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 52 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 68 | |
| 18 |
| Embodied Water, L/kg | 180 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 260 | |
| 83 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 1640 | |
| 120 to 360 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 33 | |
| 14 to 15 |
| Strength to Weight: Bending, points | 24 to 27 | |
| 15 to 16 |
| Thermal Diffusivity, mm2/s | 3.6 | |
| 14 |
| Thermal Shock Resistance, points | 17 to 21 | |
| 12 to 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0.13 to 0.18 |
| Chromium (Cr), % | 20.5 to 23.5 | |
| 0 |
| Iron (Fe), % | 52.1 to 62.1 | |
| 99.13 to 99.57 |
| Manganese (Mn), % | 4.0 to 6.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 1.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 11.5 to 13.5 | |
| 0 |
| Niobium (Nb), % | 0.1 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0.2 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |