S20910 Stainless Steel vs. C71640 Copper-nickel

S20910 stainless steel belongs to the iron alloys classification, while C71640 copper-nickel belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S20910 stainless steel and the bottom bar is C71640 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
140
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 79
52
Tensile Strength: Ultimate (UTS), MPa 780 to 940
490 to 630
Tensile Strength: Yield (Proof), MPa 430 to 810
190 to 460

Thermal Properties

Latent Heat of Fusion, J/g 300
240
Maximum Temperature: Mechanical, °C 1080
260
Melting Completion (Liquidus), °C 1420
1180
Melting Onset (Solidus), °C 1380
1120
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 13
29
Thermal Expansion, µm/m-K 16
15

Otherwise Unclassified Properties

Base Metal Price, % relative 22
40
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 4.8
5.0
Embodied Energy, MJ/kg 68
73
Embodied Water, L/kg 180
280

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 460 to 1640
130 to 750
Stiffness to Weight: Axial, points 14
8.7
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 28 to 33
15 to 20
Strength to Weight: Bending, points 24 to 27
16 to 18
Thermal Diffusivity, mm2/s 3.6
8.2
Thermal Shock Resistance, points 17 to 21
16 to 21

Alloy Composition

Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0
61.7 to 67.8
Iron (Fe), % 52.1 to 62.1
1.7 to 2.3
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 4.0 to 6.0
1.5 to 2.5
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 11.5 to 13.5
29 to 32
Niobium (Nb), % 0.1 to 0.3
0
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0
Vanadium (V), % 0.1 to 0.3
0
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0
0 to 0.5