S20910 Stainless Steel vs. K93600 Alloy

Both S20910 stainless steel and K93600 alloy are iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is S20910 stainless steel and the bottom bar is K93600 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
140
Elongation at Break, % 14 to 39
5.0 to 35
Shear Strength, MPa 500 to 570
320 to 380
Tensile Strength: Ultimate (UTS), MPa 780 to 940
480 to 810
Tensile Strength: Yield (Proof), MPa 430 to 810
280 to 750

Thermal Properties

Maximum Temperature: Mechanical, °C 1080
440
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 480
520
Thermal Conductivity, W/m-K 13
13
Thermal Expansion, µm/m-K 16
7.3

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.1

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 260
21 to 280
Resilience: Unit (Modulus of Resilience), kJ/m3 460 to 1640
280 to 2050
Stiffness to Weight: Axial, points 14
9.4
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 28 to 33
16 to 28
Strength to Weight: Bending, points 24 to 27
17 to 24
Thermal Diffusivity, mm2/s 3.6
3.1
Thermal Shock Resistance, points 17 to 21
34 to 57

Comparable Variants