S21460 Stainless Steel vs. SAE-AISI A10 Steel

Both S21460 stainless steel and SAE-AISI A10 steel are iron alloys. They have 65% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S21460 stainless steel and the bottom bar is SAE-AISI A10 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 830
810 to 2040

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1380
1440
Melting Onset (Solidus), °C 1330
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 18
12

Otherwise Unclassified Properties

Base Metal Price, % relative 14
5.0
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.0
2.1
Embodied Energy, MJ/kg 43
27
Embodied Water, L/kg 160
56

Common Calculations

PREN (Pitting Resistance) 25
5.1
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
29 to 73
Strength to Weight: Bending, points 26
25 to 46
Thermal Shock Resistance, points 17
27 to 68

Alloy Composition

Carbon (C), % 0 to 0.12
1.3 to 1.5
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 57.3 to 63.7
90.8 to 93.4
Manganese (Mn), % 14 to 16
1.6 to 2.1
Molybdenum (Mo), % 0
1.3 to 1.8
Nickel (Ni), % 5.0 to 6.0
1.6 to 2.1
Nitrogen (N), % 0.35 to 0.5
0
Phosphorus (P), % 0 to 0.060
0 to 0.030
Silicon (Si), % 0 to 1.0
1.0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030