S21603 Stainless Steel vs. EN 1.0213 Steel
Both S21603 stainless steel and EN 1.0213 steel are iron alloys. They have 63% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S21603 stainless steel and the bottom bar is EN 1.0213 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 92 to 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 45 | |
| 12 to 25 |
| Fatigue Strength, MPa | 360 | |
| 160 to 240 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 57 | |
| 72 to 80 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Shear Strength, MPa | 490 | |
| 230 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 320 to 430 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 220 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1470 |
| Melting Onset (Solidus), °C | 1380 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 17 | |
| 1.8 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 50 | |
| 18 |
| Embodied Water, L/kg | 160 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 270 | |
| 33 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
| 120 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 25 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 22 | |
| 13 to 16 |
| Thermal Shock Resistance, points | 15 | |
| 10 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.030 | |
| 0.060 to 0.1 |
| Chromium (Cr), % | 17.5 to 22 | |
| 0 |
| Iron (Fe), % | 57.6 to 67.8 | |
| 99.245 to 99.67 |
| Manganese (Mn), % | 7.5 to 9.0 | |
| 0.25 to 0.45 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 5.0 to 7.0 | |
| 0 |
| Nitrogen (N), % | 0.25 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |