S21800 Stainless Steel vs. SAE-AISI S2 Steel

Both S21800 stainless steel and SAE-AISI S2 steel are iron alloys. They have 64% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is S21800 stainless steel and the bottom bar is SAE-AISI S2 steel.

UNS S21800 (Alloy 218) Stainless Steel SAE-AISI S2 (T41902) Shock-Resisting Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		75
Shear Modulus, GPa		72

Tensile Strength: Ultimate (UTS), MPa		740
Tensile Strength: Ultimate (UTS), MPa		670 to 1940

Thermal Properties

Latent Heat of Fusion, J/g		340
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1360
Melting Completion (Liquidus), °C		1450

Melting Onset (Solidus), °C		1310
Melting Onset (Solidus), °C		1410

Specific Heat Capacity, J/kg-K		500
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		11

Otherwise Unclassified Properties

Base Metal Price, % relative		15
Base Metal Price, % relative		2.6

Density, g/cm³		7.5
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		3.1
Embodied Carbon, kg CO₂/kg material		2.1

Embodied Energy, MJ/kg		45
Embodied Energy, MJ/kg		30

Embodied Water, L/kg		150
Embodied Water, L/kg		49

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		27
Strength to Weight: Axial, points		24 to 69

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		22 to 44

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		23 to 68

Alloy Composition

Carbon (C), %		0 to 0.1
Carbon (C), %		0.4 to 0.55

Chromium (Cr), %		16 to 18
Chromium (Cr), %		0

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		59.1 to 65.4
Iron (Fe), %		96 to 98.1

Manganese (Mn), %		7.0 to 9.0
Manganese (Mn), %		0.3 to 0.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.3 to 0.6

Nickel (Ni), %		8.0 to 9.0
Nickel (Ni), %		0 to 0.3

Nitrogen (N), %		0.080 to 0.18
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.060
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		3.5 to 4.5
Silicon (Si), %		0.9 to 1.2

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030

Vanadium (V), %		0
Vanadium (V), %		0 to 0.5