S21904 Stainless Steel vs. 85-silver 15-cadmium-oxide
S21904 stainless steel belongs to the iron alloys classification, while 85-silver 15-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is S21904 stainless steel and the bottom bar is 85-silver 15-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.7 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
| 64 to 82 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 57 to 73 |
| Elongation at Break, % | 17 to 51 | |
| 2.2 to 16 |
| Shear Strength, MPa | 510 to 620 | |
| 180 to 210 |
| Strength to Weight: Axial, points | 25 to 36 | |
| 8.1 to 12 |
| Strength to Weight: Bending, points | 23 to 29 | |
| 9.7 to 13 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1000 | |
| 290 to 440 |