S21904 Stainless Steel vs. EN 1.7221 Steel

Both S21904 stainless steel and EN 1.7221 steel are iron alloys. They have 65% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S21904 stainless steel and the bottom bar is EN 1.7221 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 300
200 to 230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17 to 51
11 to 17
Fatigue Strength, MPa 380 to 550
290 to 390
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 700 to 1000
650 to 780
Tensile Strength: Yield (Proof), MPa 390 to 910
430 to 630

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 980
420
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
44
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.4
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 43
20
Embodied Water, L/kg 160
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160 to 310
83 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 2070
490 to 1050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 36
23 to 27
Strength to Weight: Bending, points 23 to 29
21 to 24
Thermal Diffusivity, mm2/s 3.8
12
Thermal Shock Resistance, points 15 to 21
19 to 23

Alloy Composition

Carbon (C), % 0 to 0.040
0.22 to 0.29
Chromium (Cr), % 19 to 21.5
0.8 to 1.2
Iron (Fe), % 59.5 to 67.4
96.8 to 98.3
Manganese (Mn), % 8.0 to 10
0.5 to 0.8
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 5.5 to 7.5
0
Nitrogen (N), % 0.15 to 0.4
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030

Comparable Variants