S24000 Stainless Steel vs. AWS E312

Both S24000 stainless steel and AWS E312 are iron alloys. They have 81% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S24000 stainless steel and the bottom bar is AWS E312.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
25
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 770
740

Thermal Properties

Latent Heat of Fusion, J/g 280
310
Melting Completion (Liquidus), °C 1390
1410
Melting Onset (Solidus), °C 1350
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 17
15

Otherwise Unclassified Properties

Base Metal Price, % relative 12
20
Density, g/cm3 7.6
7.7
Embodied Carbon, kg CO2/kg material 2.7
3.6
Embodied Energy, MJ/kg 39
52
Embodied Water, L/kg 150
200

Common Calculations

PREN (Pitting Resistance) 23
31
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
27
Strength to Weight: Bending, points 24
24
Thermal Shock Resistance, points 16
18

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.15
Chromium (Cr), % 17 to 19
28 to 32
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 61.5 to 69
52.3 to 63.5
Manganese (Mn), % 11.5 to 14.5
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 2.3 to 3.7
8.0 to 10.5
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.060
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030