S24000 Stainless Steel vs. SAE-AISI P20 Steel

Both S24000 stainless steel and SAE-AISI P20 steel are iron alloys. They have 67% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is S24000 stainless steel and the bottom bar is SAE-AISI P20 steel.

UNS S24000 (XM-29) Stainless Steel SAE-AISI P20 (T51620) Low-Carbon Mould Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		770
Tensile Strength: Ultimate (UTS), MPa		540 to 1050

Thermal Properties

Latent Heat of Fusion, J/g		280
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1390
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1350
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		12
Base Metal Price, % relative		2.8

Density, g/cm³		7.6
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		2.7
Embodied Carbon, kg CO₂/kg material		1.6

Embodied Energy, MJ/kg		39
Embodied Energy, MJ/kg		21

Embodied Water, L/kg		150
Embodied Water, L/kg		52

Common Calculations

PREN (Pitting Resistance)		23
PREN (Pitting Resistance)		2.6

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		28
Strength to Weight: Axial, points		19 to 37

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		19 to 29

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		18 to 35

Alloy Composition

Carbon (C), %		0 to 0.080
Carbon (C), %		0.28 to 0.4

Chromium (Cr), %		17 to 19
Chromium (Cr), %		0.4 to 2.0

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		61.5 to 69
Iron (Fe), %		95.2 to 98.5

Manganese (Mn), %		11.5 to 14.5
Manganese (Mn), %		0.35 to 0.71

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.3 to 0.55

Nickel (Ni), %		2.3 to 3.7
Nickel (Ni), %		0

Nitrogen (N), %		0.2 to 0.4
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.060
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.75
Silicon (Si), %		0.2 to 0.8

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030