S28200 Stainless Steel vs. ASTM F15 Fe-Ni-Co
Both S28200 stainless steel and ASTM F15 Fe-Ni-Co are iron alloys. They have 54% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is S28200 stainless steel and the bottom bar is ASTM F15 Fe-Ni-Co.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 520 to 880 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1410 |
| Melting Onset (Solidus), °C | 1330 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Expansion, µm/m-K | 18 | |
| 6.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 49 |
| Density, g/cm3 | 7.6 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 5.2 |
| Embodied Energy, MJ/kg | 41 | |
| 71 |
| Embodied Water, L/kg | 160 | |
| 190 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 26 | |
| 23 |
| Strength to Weight: Axial, points | 32 | |
| 17 to 29 |
| Strength to Weight: Bending, points | 27 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 17 | |
| 32 to 55 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.040 |
| Chromium (Cr), % | 17 to 19 | |
| 0 to 0.2 |
| Cobalt (Co), % | 0 | |
| 16 to 18 |
| Copper (Cu), % | 0.75 to 1.3 | |
| 0 to 0.2 |
| Iron (Fe), % | 57.7 to 64.1 | |
| 50.3 to 56 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 17 to 19 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.75 to 1.3 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 28 to 30 |
| Nitrogen (N), % | 0.4 to 0.6 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |