S28200 Stainless Steel vs. AWS E349

Both S28200 stainless steel and AWS E349 are iron alloys. They have 82% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S28200 stainless steel and the bottom bar is AWS E349.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
29
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 870
770

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Melting Completion (Liquidus), °C 1380
1470
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 18
14

Otherwise Unclassified Properties

Base Metal Price, % relative 12
25
Density, g/cm3 7.6
7.9
Embodied Carbon, kg CO2/kg material 2.8
4.9
Embodied Energy, MJ/kg 41
72
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 29
24
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 26
25
Strength to Weight: Axial, points 32
27
Strength to Weight: Bending, points 27
24
Thermal Shock Resistance, points 17
20

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.13
Chromium (Cr), % 17 to 19
18 to 21
Copper (Cu), % 0.75 to 1.3
0 to 0.75
Iron (Fe), % 57.7 to 64.1
60.5 to 71.1
Manganese (Mn), % 17 to 19
0.5 to 2.5
Molybdenum (Mo), % 0.75 to 1.3
0.35 to 0.65
Nickel (Ni), % 0
8.0 to 10
Niobium (Nb), % 0
0.75 to 1.2
Nitrogen (N), % 0.4 to 0.6
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0 to 0.15
Tungsten (W), % 0
1.3 to 1.8
Vanadium (V), % 0
0.1 to 0.3