S28200 Stainless Steel vs. AWS ERTi-12

S28200 stainless steel belongs to the iron alloys classification, while AWS ERTi-12 belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S28200 stainless steel and the bottom bar is AWS ERTi-12.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 45
12
Fatigue Strength, MPa 430
200
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 77
41
Tensile Strength: Ultimate (UTS), MPa 870
480
Tensile Strength: Yield (Proof), MPa 460
340

Thermal Properties

Latent Heat of Fusion, J/g 290
420
Maximum Temperature: Mechanical, °C 900
320
Melting Completion (Liquidus), °C 1380
1670
Melting Onset (Solidus), °C 1330
1620
Specific Heat Capacity, J/kg-K 480
540
Thermal Expansion, µm/m-K 18
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
37
Density, g/cm3 7.6
4.5
Embodied Carbon, kg CO2/kg material 2.8
31
Embodied Energy, MJ/kg 41
510
Embodied Water, L/kg 160
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
52
Resilience: Unit (Modulus of Resilience), kJ/m3 540
550
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 26
35
Strength to Weight: Axial, points 32
30
Strength to Weight: Bending, points 27
30
Thermal Shock Resistance, points 17
37

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0.75 to 1.3
0
Hydrogen (H), % 0
0 to 0.0080
Iron (Fe), % 57.7 to 64.1
0 to 0.15
Manganese (Mn), % 17 to 19
0
Molybdenum (Mo), % 0.75 to 1.3
0.2 to 0.4
Nickel (Ni), % 0
0.060 to 0.090
Nitrogen (N), % 0.4 to 0.6
0 to 0.015
Oxygen (O), % 0
0.080 to 0.16
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
99.147 to 99.66