S28200 Stainless Steel vs. C14180 Copper

S28200 stainless steel belongs to the iron alloys classification, while C14180 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S28200 stainless steel and the bottom bar is C14180 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 45
15
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
43
Tensile Strength: Ultimate (UTS), MPa 870
210
Tensile Strength: Yield (Proof), MPa 460
130

Thermal Properties

Latent Heat of Fusion, J/g 290
210
Maximum Temperature: Mechanical, °C 900
200
Melting Completion (Liquidus), °C 1380
1080
Melting Onset (Solidus), °C 1330
1080
Specific Heat Capacity, J/kg-K 480
390
Thermal Expansion, µm/m-K 18
17

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 7.6
9.0
Embodied Carbon, kg CO2/kg material 2.8
2.6
Embodied Energy, MJ/kg 41
41
Embodied Water, L/kg 160
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
28
Resilience: Unit (Modulus of Resilience), kJ/m3 540
69
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 26
18
Strength to Weight: Axial, points 32
6.5
Strength to Weight: Bending, points 27
8.8
Thermal Shock Resistance, points 17
7.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0.75 to 1.3
99.9 to 100
Iron (Fe), % 57.7 to 64.1
0
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 17 to 19
0
Molybdenum (Mo), % 0.75 to 1.3
0
Nitrogen (N), % 0.4 to 0.6
0
Phosphorus (P), % 0 to 0.045
0 to 0.075
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0