S28200 Stainless Steel vs. R60802 Alloy

S28200 stainless steel belongs to the iron alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is S28200 stainless steel and the bottom bar is R60802 alloy.

UNS S28200 Stainless Steel UNS R60802 Zirconium-Tin Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		98

Elongation at Break, %		45
Elongation at Break, %		22

Poisson's Ratio		0.28
Poisson's Ratio		0.34

Shear Modulus, GPa		77
Shear Modulus, GPa		36

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		430

Tensile Strength: Yield (Proof), MPa		460
Tensile Strength: Yield (Proof), MPa		270

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		250

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		270

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		6.0

Otherwise Unclassified Properties

Density, g/cm³		7.6
Density, g/cm³		6.5

Embodied Water, L/kg		160
Embodied Water, L/kg		290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		330
Resilience: Ultimate (Unit Rupture Work), MJ/m³		85

Resilience: Unit (Modulus of Resilience), kJ/m³		540
Resilience: Unit (Modulus of Resilience), kJ/m³		380

Stiffness to Weight: Axial, points		15
Stiffness to Weight: Axial, points		8.3

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		32
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		27
Strength to Weight: Bending, points		19

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		53

Alloy Composition

Carbon (C), %		0 to 0.15
Carbon (C), %		0

Chromium (Cr), %		17 to 19
Chromium (Cr), %		0.050 to 0.15

Copper (Cu), %		0.75 to 1.3
Copper (Cu), %		0

Iron (Fe), %		57.7 to 64.1
Iron (Fe), %		0.070 to 0.2

Manganese (Mn), %		17 to 19
Manganese (Mn), %		0

Molybdenum (Mo), %		0.75 to 1.3
Molybdenum (Mo), %		0

Nickel (Ni), %		0
Nickel (Ni), %		0.030 to 0.080

Nitrogen (N), %		0.4 to 0.6
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.045
Phosphorus (P), %		0

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		1.2 to 1.7

Zirconium (Zr), %		0
Zirconium (Zr), %		97.8 to 98.7

Residuals, %		0
Residuals, %		0 to 0.11