S30435 Stainless Steel vs. 5056 Aluminum

S30435 stainless steel belongs to the iron alloys classification, while 5056 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S30435 stainless steel and the bottom bar is 5056 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
67
Elongation at Break, % 51
4.9 to 31
Fatigue Strength, MPa 170
140 to 200
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
25
Shear Strength, MPa 370
170 to 240
Tensile Strength: Ultimate (UTS), MPa 510
290 to 460
Tensile Strength: Yield (Proof), MPa 170
150 to 410

Thermal Properties

Latent Heat of Fusion, J/g 280
400
Maximum Temperature: Mechanical, °C 900
190
Melting Completion (Liquidus), °C 1420
640
Melting Onset (Solidus), °C 1380
570
Specific Heat Capacity, J/kg-K 480
910
Thermal Conductivity, W/m-K 16
130
Thermal Expansion, µm/m-K 16
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
29
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
99

Otherwise Unclassified Properties

Base Metal Price, % relative 14
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 2.9
9.0
Embodied Energy, MJ/kg 40
150
Embodied Water, L/kg 140
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
12 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 77
170 to 1220
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
51
Strength to Weight: Axial, points 18
30 to 48
Strength to Weight: Bending, points 18
36 to 50
Thermal Diffusivity, mm2/s 4.2
53
Thermal Shock Resistance, points 12
13 to 20

Alloy Composition

Aluminum (Al), % 0
93 to 95.4
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 16 to 18
0.050 to 0.2
Copper (Cu), % 1.5 to 3.0
0 to 0.1
Iron (Fe), % 66.9 to 75.5
0 to 0.4
Magnesium (Mg), % 0
4.5 to 5.6
Manganese (Mn), % 0 to 2.0
0.050 to 0.2
Nickel (Ni), % 7.0 to 9.0
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15