S30435 Stainless Steel vs. EN 1.0143 Steel

Both S30435 stainless steel and EN 1.0143 steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S30435 stainless steel and the bottom bar is EN 1.0143 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 51
21
Fatigue Strength, MPa 170
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 370
300
Tensile Strength: Ultimate (UTS), MPa 510
470
Tensile Strength: Yield (Proof), MPa 170
250

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 14
1.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.9
1.4
Embodied Energy, MJ/kg 40
18
Embodied Water, L/kg 140
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
85
Resilience: Unit (Modulus of Resilience), kJ/m3 77
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 18
17
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.21
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 1.5 to 3.0
0 to 0.6
Iron (Fe), % 66.9 to 75.5
97.5 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.6
Nickel (Ni), % 7.0 to 9.0
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.040