S30435 Stainless Steel vs. R30556 Alloy

Both S30435 stainless steel and R30556 alloy are iron alloys. Both are furnished in the annealed condition. They have 56% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30435 stainless steel and the bottom bar is R30556 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 51
45
Fatigue Strength, MPa 170
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
81
Shear Strength, MPa 370
550
Tensile Strength: Ultimate (UTS), MPa 510
780
Tensile Strength: Yield (Proof), MPa 170
350

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1330
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 16
11
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 14
70
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 2.9
8.7
Embodied Energy, MJ/kg 40
130
Embodied Water, L/kg 140
300

Common Calculations

PREN (Pitting Resistance) 17
40
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
290
Resilience: Unit (Modulus of Resilience), kJ/m3 77
290
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 18
26
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 4.2
2.9
Thermal Shock Resistance, points 12
18

Alloy Composition

Aluminum (Al), % 0
0.1 to 0.5
Boron (B), % 0
0 to 0.020
Carbon (C), % 0 to 0.080
0.050 to 0.15
Chromium (Cr), % 16 to 18
21 to 23
Cobalt (Co), % 0
16 to 21
Copper (Cu), % 1.5 to 3.0
0
Iron (Fe), % 66.9 to 75.5
20.4 to 38.2
Lanthanum (La), % 0
0.0050 to 0.1
Manganese (Mn), % 0 to 2.0
0.5 to 2.0
Molybdenum (Mo), % 0
2.5 to 4.0
Nickel (Ni), % 7.0 to 9.0
19 to 22.5
Niobium (Nb), % 0
0 to 0.3
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0.2 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.015
Tantalum (Ta), % 0
0.3 to 1.3
Tungsten (W), % 0
2.0 to 3.5
Zinc (Zn), % 0
0.0010 to 0.1