S30441 Stainless Steel vs. Solder Alloy 124

S30441 stainless steel belongs to the iron alloys classification, while solder alloy 124 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S30441 stainless steel and the bottom bar is solder alloy 124.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
17
Elongation at Break, % 45
46
Poisson's Ratio 0.28
0.44
Shear Modulus, GPa 76
5.8
Tensile Strength: Ultimate (UTS), MPa 580
27

Thermal Properties

Latent Heat of Fusion, J/g 300
24
Melting Completion (Liquidus), °C 1420
330
Melting Onset (Solidus), °C 1370
320
Specific Heat Capacity, J/kg-K 480
130
Thermal Conductivity, W/m-K 15
22
Thermal Expansion, µm/m-K 16
29

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
7.7

Otherwise Unclassified Properties

Base Metal Price, % relative 18
70
Density, g/cm3 7.8
11
Embodied Carbon, kg CO2/kg material 3.4
4.1
Embodied Energy, MJ/kg 50
68
Embodied Water, L/kg 150
470

Common Calculations

Stiffness to Weight: Axial, points 14
0.83
Stiffness to Weight: Bending, points 25
7.6
Strength to Weight: Axial, points 21
0.65
Strength to Weight: Bending, points 20
1.8
Thermal Diffusivity, mm2/s 4.0
15
Thermal Shock Resistance, points 13
3.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.12
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 1.5 to 2.5
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 62 to 71.7
0 to 0.020
Lead (Pb), % 0
97.2 to 98.2
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10.5
0 to 0.010
Niobium (Nb), % 0.1 to 0.5
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 1.0 to 2.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
1.8 to 2.2
Tungsten (W), % 0.2 to 0.8
0
Zinc (Zn), % 0
0 to 0.0010