S30601 Stainless Steel vs. CC497K Bronze
S30601 stainless steel belongs to the iron alloys classification, while CC497K bronze belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is S30601 stainless steel and the bottom bar is CC497K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 55 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 93 |
| Elongation at Break, % | 37 | |
| 6.7 |
| Poisson's Ratio | 0.28 | |
| 0.36 |
| Shear Modulus, GPa | 75 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 300 | |
| 91 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 160 |
| Maximum Temperature: Mechanical, °C | 950 | |
| 130 |
| Melting Completion (Liquidus), °C | 1360 | |
| 870 |
| Melting Onset (Solidus), °C | 1310 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 330 |
| Thermal Expansion, µm/m-K | 15 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 20 | |
| 29 |
| Density, g/cm3 | 7.6 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 3.0 |
| Embodied Energy, MJ/kg | 55 | |
| 48 |
| Embodied Water, L/kg | 150 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 10 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 | |
| 45 |
| Stiffness to Weight: Axial, points | 14 | |
| 5.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 16 |
| Strength to Weight: Axial, points | 24 | |
| 5.6 |
| Strength to Weight: Bending, points | 22 | |
| 7.8 |
| Thermal Shock Resistance, points | 16 | |
| 7.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.75 |
| Carbon (C), % | 0 to 0.015 | |
| 0 |
| Chromium (Cr), % | 17 to 18 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 67.5 to 77.5 |
| Iron (Fe), % | 56.9 to 60.5 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 18 to 23 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 17 to 18 | |
| 0.5 to 2.5 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.1 |
| Silicon (Si), % | 5.0 to 5.6 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.013 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 4.0 to 6.0 |
| Zinc (Zn), % | 0 | |
| 0 to 2.0 |