S30815 Stainless Steel vs. EN 1.6750 Steel

Both S30815 stainless steel and EN 1.6750 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S30815 stainless steel and the bottom bar is EN 1.6750 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
18
Fatigue Strength, MPa 320
310
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 680
650
Tensile Strength: Yield (Proof), MPa 350
460

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1020
420
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 17
3.3
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.3
1.7
Embodied Energy, MJ/kg 47
22
Embodied Water, L/kg 160
52

Common Calculations

PREN (Pitting Resistance) 24
2.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
110
Resilience: Unit (Modulus of Resilience), kJ/m3 310
570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
23
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 4.0
10
Thermal Shock Resistance, points 15
19

Alloy Composition

Carbon (C), % 0.050 to 0.1
0.17 to 0.23
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 20 to 22
0.3 to 0.5
Iron (Fe), % 62.8 to 68.4
95.3 to 97.5
Manganese (Mn), % 0 to 0.8
0.8 to 1.2
Molybdenum (Mo), % 0
0.4 to 0.8
Nickel (Ni), % 10 to 12
0.8 to 1.2
Nitrogen (N), % 0.14 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.4 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030