S30815 Stainless Steel vs. SAE-AISI 1552 Steel

Both S30815 stainless steel and SAE-AISI 1552 steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S30815 stainless steel and the bottom bar is SAE-AISI 1552 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
220 to 250
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
11 to 14
Fatigue Strength, MPa 320
290 to 400
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
34 to 46
Shear Modulus, GPa 77
72
Shear Strength, MPa 480
460 to 510
Tensile Strength: Ultimate (UTS), MPa 680
760 to 840
Tensile Strength: Yield (Proof), MPa 350
460 to 650

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1020
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
12

Otherwise Unclassified Properties

Base Metal Price, % relative 17
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.4
Embodied Energy, MJ/kg 47
19
Embodied Water, L/kg 160
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
81 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 310
560 to 1130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
27 to 30
Strength to Weight: Bending, points 22
24 to 25
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 15
26 to 29

Alloy Composition

Carbon (C), % 0.050 to 0.1
0.47 to 0.55
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 20 to 22
0
Iron (Fe), % 62.8 to 68.4
97.9 to 98.3
Manganese (Mn), % 0 to 0.8
1.2 to 1.5
Nickel (Ni), % 10 to 12
0
Nitrogen (N), % 0.14 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.4 to 2.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050