S31254 Stainless Steel vs. EN 1.4438 Stainless Steel

Both S31254 stainless steel and EN 1.4438 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S31254 stainless steel and the bottom bar is EN 1.4438 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
41
Fatigue Strength, MPa 290
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
79
Shear Strength, MPa 490
420
Tensile Strength: Ultimate (UTS), MPa 720
620
Tensile Strength: Yield (Proof), MPa 330
250

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 1090
1000
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 28
22
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.5
4.4
Embodied Energy, MJ/kg 74
60
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 44
31
Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
200
Resilience: Unit (Modulus of Resilience), kJ/m3 270
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 3.8
3.7
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.030
Chromium (Cr), % 19.5 to 20.5
17.5 to 19.5
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 51.4 to 56.3
57.3 to 66.5
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 6.0 to 6.5
3.0 to 4.0
Nickel (Ni), % 17.5 to 18.5
13 to 16
Nitrogen (N), % 0.18 to 0.22
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015