S31266 Stainless Steel vs. R31539 Cobalt
S31266 stainless steel belongs to the iron alloys classification, while R31539 cobalt belongs to the cobalt alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is S31266 stainless steel and the bottom bar is R31539 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 220 |
| Elongation at Break, % | 40 | |
| 13 to 22 |
| Fatigue Strength, MPa | 400 | |
| 310 to 480 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 56 | |
| 13 to 23 |
| Shear Modulus, GPa | 81 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 1000 to 1340 |
| Tensile Strength: Yield (Proof), MPa | 470 | |
| 590 to 940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 320 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1360 |
| Melting Onset (Solidus), °C | 1420 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 450 |
| Thermal Conductivity, W/m-K | 12 | |
| 13 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.8 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 6.5 | |
| 8.2 |
| Embodied Energy, MJ/kg | 89 | |
| 110 |
| Embodied Water, L/kg | 220 | |
| 530 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 290 | |
| 140 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 | |
| 780 to 2000 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 29 | |
| 33 to 44 |
| Strength to Weight: Bending, points | 24 | |
| 27 to 32 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 3.5 |
| Thermal Shock Resistance, points | 18 | |
| 24 to 32 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.3 to 1.0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.14 |
| Chromium (Cr), % | 23 to 25 | |
| 26 to 30 |
| Cobalt (Co), % | 0 | |
| 57.7 to 68.7 |
| Copper (Cu), % | 1.0 to 2.5 | |
| 0 |
| Iron (Fe), % | 34.1 to 46 | |
| 0 to 0.75 |
| Lanthanum (La), % | 0 | |
| 0.030 to 0.2 |
| Manganese (Mn), % | 2.0 to 4.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 5.2 to 6.2 | |
| 5.0 to 7.0 |
| Nickel (Ni), % | 21 to 24 | |
| 0 to 1.0 |
| Nitrogen (N), % | 0.35 to 0.6 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tungsten (W), % | 1.5 to 2.5 | |
| 0 |