S31277 Stainless Steel vs. EN 1.7213 Steel

Both S31277 stainless steel and EN 1.7213 steel are iron alloys. They have 43% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S31277 stainless steel and the bottom bar is EN 1.7213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 860
500 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.5
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.7
1.5
Embodied Energy, MJ/kg 90
20
Embodied Water, L/kg 220
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
18 to 55
Strength to Weight: Bending, points 25
18 to 38
Thermal Shock Resistance, points 19
15 to 45

Alloy Composition

Carbon (C), % 0 to 0.020
0.22 to 0.29
Chromium (Cr), % 20.5 to 23
0.9 to 1.2
Copper (Cu), % 0.5 to 1.5
0 to 0.25
Iron (Fe), % 35.5 to 46.2
96.7 to 98.1
Manganese (Mn), % 0 to 3.0
0.6 to 0.9
Molybdenum (Mo), % 6.5 to 8.0
0.15 to 0.3
Nickel (Ni), % 26 to 28
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.010
0.020 to 0.040