S31655 Stainless Steel vs. Nickel 689

S31655 stainless steel belongs to the iron alloys classification, while nickel 689 belongs to the nickel alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S31655 stainless steel and the bottom bar is nickel 689.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
350
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 39
23
Fatigue Strength, MPa 300
420
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
80
Shear Strength, MPa 490
790
Tensile Strength: Ultimate (UTS), MPa 710
1250
Tensile Strength: Yield (Proof), MPa 350
690

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Maximum Temperature: Mechanical, °C 1010
990
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1380
1390
Specific Heat Capacity, J/kg-K 480
450
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 17
70
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 3.3
11
Embodied Energy, MJ/kg 46
150
Embodied Water, L/kg 160
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
240
Resilience: Unit (Modulus of Resilience), kJ/m3 310
1170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 25
41
Strength to Weight: Bending, points 23
30
Thermal Shock Resistance, points 16
35

Alloy Composition

Aluminum (Al), % 0
0.75 to 1.3
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 0 to 0.030
0.1 to 0.2
Chromium (Cr), % 19.5 to 21.5
18 to 20
Cobalt (Co), % 0
9.0 to 11
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 63.2 to 71.9
0 to 5.0
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 0.5 to 1.5
9.0 to 10.5
Nickel (Ni), % 8.0 to 9.5
48.3 to 60.9
Nitrogen (N), % 0.14 to 0.25
0
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
2.3 to 2.8