S31727 Stainless Steel vs. AWS E110C-K4
Both S31727 stainless steel and AWS E110C-K4 are iron alloys. They have 61% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is S31727 stainless steel and the bottom bar is AWS E110C-K4.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Elongation at Break, % | 40 | |
17 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 78 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 630 | |
850 |
Tensile Strength: Yield (Proof), MPa | 270 | |
780 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
250 |
Melting Completion (Liquidus), °C | 1440 | |
1460 |
Melting Onset (Solidus), °C | 1390 | |
1410 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Expansion, µm/m-K | 16 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 24 | |
3.5 |
Density, g/cm3 | 8.0 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 4.7 | |
1.7 |
Embodied Energy, MJ/kg | 64 | |
23 |
Embodied Water, L/kg | 180 | |
54 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
140 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
1600 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 22 | |
30 |
Strength to Weight: Bending, points | 20 | |
25 |
Thermal Shock Resistance, points | 14 | |
25 |
Alloy Composition
Carbon (C), % | 0 to 0.030 | |
0 to 0.15 |
Chromium (Cr), % | 17.5 to 19 | |
0.15 to 0.65 |
Copper (Cu), % | 2.8 to 4.0 | |
0 to 0.35 |
Iron (Fe), % | 53.7 to 61.3 | |
92.1 to 98.4 |
Manganese (Mn), % | 0 to 1.0 | |
0.75 to 2.3 |
Molybdenum (Mo), % | 3.8 to 4.5 | |
0.25 to 0.65 |
Nickel (Ni), % | 14.5 to 16.5 | |
0.5 to 2.5 |
Nitrogen (N), % | 0.15 to 0.21 | |
0 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.025 |
Silicon (Si), % | 0 to 1.0 | |
0 to 0.8 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.025 |
Vanadium (V), % | 0 | |
0 to 0.030 |
Residuals, % | 0 | |
0 to 0.5 |