S31730 Stainless Steel vs. SAE-AISI O6 Steel

Both S31730 stainless steel and SAE-AISI O6 steel are iron alloys. They have 59% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is S31730 stainless steel and the bottom bar is SAE-AISI O6 steel.

UNS S31730 Stainless Steel SAE-AISI O6 (T31506) Oil-Hardening Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		180

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		71

Tensile Strength: Ultimate (UTS), MPa		540
Tensile Strength: Ultimate (UTS), MPa		670 to 2070

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1430
Melting Completion (Liquidus), °C		1430

Melting Onset (Solidus), °C		1390
Melting Onset (Solidus), °C		1390

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		24
Base Metal Price, % relative		2.3

Density, g/cm³		8.0
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		4.6
Embodied Carbon, kg CO₂/kg material		1.5

Embodied Energy, MJ/kg		63
Embodied Energy, MJ/kg		21

Embodied Water, L/kg		180
Embodied Water, L/kg		47

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		19
Strength to Weight: Axial, points		24 to 74

Strength to Weight: Bending, points		18
Strength to Weight: Bending, points		22 to 47

Thermal Shock Resistance, points		12
Thermal Shock Resistance, points		22 to 69

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		1.3 to 1.6

Chromium (Cr), %		17 to 19
Chromium (Cr), %		0 to 0.3

Copper (Cu), %		4.0 to 5.0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		52.4 to 61
Iron (Fe), %		94.6 to 97.7

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		0.3 to 1.1

Molybdenum (Mo), %		3.0 to 4.0
Molybdenum (Mo), %		0.2 to 0.3

Nickel (Ni), %		15 to 16.5
Nickel (Ni), %		0 to 0.3

Nitrogen (N), %		0 to 0.045
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.55 to 1.5

Sulfur (S), %		0 to 0.010
Sulfur (S), %		0 to 0.030